The Preparation Process, Microstructure and Properties of Cellular TiC-High Mn Steel-Bonded Carbide

TiC-high Mn steel-bonded carbide with a cellular structure was designed and fabricated by powder metallurgy techniques using coarse and fine TiC particles as the hard phase. This preparation process of the alloy was designed carefully and optimized. The microstructure of the alloy was observed using a scanning electron microscope. The results show that there are two types of microstructures observed in this TiC steel-bonded carbide: the coarse-grained TiC structure and fine-grained TiC structure. The transverse rupture strength and impact toughness of the alloy reach maximum values 2231 MPa and 12.87 J/cm², respectively, when the starting weight ratio of MP-A (containing coarse TiC particles) to MP-B (containing fine TiC particles) is 60:40. Hence, this study serves as a feasible and economical example to prepare a high-strength and high-toughness TiC-high Mn steel-bonded carbide with little production cost increase.