Highly Dual Antifouling and Antibacterial Ultrafiltration Membranes Modified with Silane Coupling Agent and...

Dual antifouling and antibacterial polysulfone(PSf)/polyethersulfone(PES) hybrid membranes were developed by the synergy of capsaicin-mimic N-(5-methyl acrylamide-2,3,4 hydroxy benzyl) acrylamide (AMTHBA) and vinyl triethylene (b-methoxy ethoxy) silane (VTMES). First, AMTHBA as a natural antimicrobial agent was incorporated into a casting solution via "microwave-assistance (MWA) in situ polymerization-blending" process to construct a hydroxyl-rich environment. Then, VTMES crosslinked to a hydroxyl-rich polymer matrix via hydrolytic condensation, and the influence of VTMES content on the hybrid membrane properties was systematically investigated. When the VTMES added amount was 1.0 wt %, the hybrid membrane achieved an optimal separation performance including a steady-state humic acid (HA) (5 mg/L) permeation flux of 326 L·m^-2·h^-1 and a rejection percentage of 97%. The antibacterial tests revealed that the hybrid membranes exhibited sustained bactericidal activity and effective inhibition of bacterial adhesion. Besides, the dual-functional membranes were clean as new after two-cycles filtration (with a cleaning efficiency of ~90%), indicating that the network silicone film on the surface benefits the foulant repellence. Hopefully, the dual-functional membranes constructed in this study can be applicable to the pretreatment stage of water treatment.