Reducing Anomalous Hysteresis in Perovskite Solar Cells by Suppressing the Interfacial Ferroelectric Order

Despite the booming research in organometal halide perovskite solar cells (PSCs) of recent years, considerable roadblocks remain for their large-scale deployment, ranging from undesirable current-voltage hysteresis to inferior device stability. Among various plausible origins of hysteresis, interfacial ferroelectricity is particularly intriguing and warrants a close scrutiny. Here, we examine interfacial ferroelectricity in MAPbI₃ (FAPbI₃)/TiO₂ and MAPbI₃/phenyl-C61-butyric-acid-methyl-ester (PCBM) heterostructures and explore the correlations between the interfacial ferroelectricity and the hysteresis from the perspective of nonadiabatic electronic dynamics. It is found that the ferroelectric order develops at the MAPbI₃/TiO₂ interface owing to the interaction between the polar MA ions and TiO₂. The polarization switching of the MA ions under an applied gate field would drastically result in different rates in interfacial photoelectron injection and electron-hole recombination, contributing to the undesirable hysteresis. In sharp contrast, ferroelectricity is suppressed at the FAPbI₃/TiO₂ and MAPbI₃/PCBM interfaces, thanks to elimination of the interfacial electric field between perovskite and TiO₂ via substitution of strong polar MA (dipole moment: 2.29 debye) by weak polar FA ions (dipole moment: 0.29 debye) and interface passivation, leading to consistent interfacial electronic dynamics and the absence of hysteresis. The present work sheds light on the physical cause for hysteresis and points to the direction to which the hysteresis could be mitigated in PSCs.