Relationship between the Size and Inner Structure of Particles of Virgin and Re-Used MS1 Maraging Steel Powder for...

Additive manufacturing (AM) is today in the main focus-and not only in commercial production. Products with complex geometry can be built using various AM techniques, which include laser sintering of metal powder. Although the technique has been known for a quite long time, the impact of the morphology of individual powder particles on the process has not yet been adequately documented. This article presents a detailed microscopic analysis of virgin and reused powder particles of MS1 maraging steel. The metallographic observation was performed using a scanning electron microscope (SEM). The particle size of the individual powder particles was measured in the SEM and the particle surface morphology and its change in the reused powder were observed. Individual particles were analyzed in detail using an SEM with a focused ion beam (FIB) milling capability. The powder particles were gradually cut off in thin layers so that their internal structure, chemical element distribution, possible internal defects, and shape could be monitored. Elemental distribution and phase distribution were analyzed using EDS and EBSD, respectively. Our findings lead to a better understanding and prediction of defects in additive-manufactured products. This could be helpful not just in the AM field, but in any metal powder-based processes, such as metal injection molding, powder metallurgy, spray deposition processes, and others.