Orientation and Microstructure Evolution of Al-Al2Cu Regular Eutectic Lamellar Bifurcating in an Abruptly Changing

Ka Gao1,2, Zan Zhang1,2, Junliang Zhao1,2

  • 1School of Materials Science and Engineering, Zhengzhou University of Aeronautics, Zhengzhou 450015, China.

Materials (Basel, Switzerland)
|February 28, 2020
PubMed

Keywords:
directional solidificationgrain growthgrowth orientationlamellar bifurcationsolidification rate

More Related Videos

Processing of Bulk Nanocrystalline Metals at the US Army Research Laboratory08:58

Processing of Bulk Nanocrystalline Metals at the US Army Research Laboratory

Published on: March 7, 2018

9.7K
Experimental Procedure for Warm Spinning of Cast Aluminum Components07:36

Experimental Procedure for Warm Spinning of Cast Aluminum Components

Published on: February 1, 2017

9.8K

Related Concept Videos

Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
1.8K
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.
480
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
423
Temperature Dependent Deformation01:12

Temperature Dependent Deformation

In a nonhomogeneous rod made up of steel and brass, restrained at both ends and subjected to a temperature change, several steps are involved in calculating the stress and compressive load. Due to the problem's static indeterminacy, one end support is disconnected, allowing the rod to experience the temperature change freely. Next, an unknown force is applied at the free end, triggering deformations in the rod's steel and brass portions. These deformations are then calculated and added...
328
Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
967
Unsymmetric Loading of Thin-Walled Members01:23

Unsymmetric Loading of Thin-Walled Members

Thin-walled members with non-symmetrical cross-sections are vital to engineering structures, offering material efficiency and structural integrity. However, unsymmetrical loading on these members leads to complex stress distributions, resulting in simultaneous bending and twisting can cause deformation or structural failure. The interaction between bending and twisting requires detailed analysis to ensure structural resilience.
The concept of the shear center is crucial in countering the...
336