Proton Conducting Perhydropolysilazane-Derived Gate Dielectric for Solution-Processed Metal Oxide-Based Thin-Film...

Perhydropolysilazane (PHPS), an inorganic polymer composed of Si-N and Si-H, has attracted much attention as a precursor for gate dielectrics of thin-film transistors (TFTs) due to its facile processing even at a relatively low temperature. However, an in-depth understanding of the tunable dielectric behavior of PHPS-derived dielectrics and their effects on TFT device performance is still lacking. In this study, the PHPS-derived dielectric films formed at different annealing temperatures have been used as the gate dielectric layer for solution-processed indium zinc oxide (IZO) TFTs. Notably, the IZO TFTs fabricated on PHPS annealed at 350 °C exhibit mobility as high as 118 cm² V^-1 s^-1, which is about 50 times the IZO TFTs made on typical SiO₂ dielectrics. The outstanding electrical performance is possible because of the exceptional capacitance of PHPS-derived dielectric caused by the limited hydrolysis reaction of PHPS at a low processing temperature (<400 °C). According to our analysis, the exceptional dielectric behavior is originated from the electric double layer formed by mobile of protons in the low temperature-annealed PHPS dielectrics. Furthermore, proton conduction through the PHPS dielectric occurs through a three-dimensional pathway by a hopping mechanism, which allows uniform polarization of the dielectric even at room temperature, leading to amplified performance of the IZO TFTs.