Study on Wear and Fatigue Performance of Two Types of High-Speed Railway Wheel Materials at Different Ambient

Lei Ma1, Wenjian Wang2, Jun Guo2

  • 1School of Mechanical Engineering, Xihua University, Chengdu 610039, China.

Materials (Basel, Switzerland)
|March 11, 2020
PubMed

Keywords:
alpine regionfatigue damagehigh-speed wheel and rail materialstemperaturewear

More Related Videos

Experimental Procedure for Warm Spinning of Cast Aluminum Components07:36

Experimental Procedure for Warm Spinning of Cast Aluminum Components

Published on: February 1, 2017

9.8K
Artificial Thermal Ageing of Polyester Reinforced and Polyvinyl Chloride Coated Technical Fabric07:48

Artificial Thermal Ageing of Polyester Reinforced and Polyvinyl Chloride Coated Technical Fabric

Published on: January 29, 2020

7.0K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
760
Rolling Resistance: Problem Solving01:17

Rolling Resistance: Problem Solving

Rolling resistance, also known as rolling friction, is the force that resists the motion of a rolling object, such as a wheel, tire, or ball, when it moves over a surface. It is caused by the deformation of the object and the surface in contact with each other, as well as other factors like internal friction, hysteresis, and energy losses within the materials. Rolling resistance opposes the object's motion, requiring additional energy to overcome it and maintain movement. In practical...
724
Rolling Resistance01:21

Rolling Resistance

When a solid cylinder rolls steadily on a rigid surface, the normal force applied by the surface on the cylinder is perpendicular to the tangent at the contact point. However, since no materials are entirely rigid, the surface's reaction to the cylinder involves a range of normal pressures.
For instance, imagine a hard cylinder rolling on a comparatively soft surface. The cylinder's weight compresses the surface beneath it. As the cylinder moves, the material in front of it slows down due to...
557
Thermal Stress01:09

Thermal Stress

If the temperature of an object is changed while it is prevented from expanding or contracting, the object is subjected to stress. The stress is compressive if the object expands in the absence of constraint and tensile if it contracts. This stress resulting from temperature change is known as thermal stress. It can be quite large and can cause damage. To avoid this stress, engineers may design components so they can expand and contract freely. For instance, on highways, gaps are deliberately...
3.2K
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
435
Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
965