Bi³⁺ -Er³⁺ and Bi³⁺ -Yb³⁺ Codoped Cs₂ AgInCl₆ Double Perovskite Near-Infrared Emitters

Bi³⁺ and lanthanide ions have been codoped in metal oxides as optical sensitizers and emitters. But such codoping is not known in typical semiconductors such as Si, GaAs, and CdSe. Metal halide perovskite with coordination number 6 provides an opportunity to codope Bi³⁺ and lanthanide ions. Codoping of Bi³⁺ and Ln³⁺ (Ln=Er and Yb) in Cs₂ AgInCl₆ double perovskite is presented. Bi³⁺ -Er³⁺ codoped Cs₂ AgInCl₆ shows Er³⁺ f-electron emission at 1540 nm (suitable for low-loss optical communication). Bi³⁺ codoping decreases the excitation (absorption) energy, such that the samples can be excited with ca. 370 nm light. At that excitation, Bi³⁺ -Er³⁺ codoped Cs₂ AgInCl₆ shows ca. 45 times higher emission intensity compared to the Er³⁺ doped Cs₂ AgInCl₆ . Similar results are also observed in Bi³⁺ -Yb³⁺ codoped sample emitting at 994 nm. A combination of temperature-dependent (5.7 K to 423 K) photoluminescence and calculations is used to understand the optical sensitization and emission processes.