Structural and tribological characteristics of ultra-low-wear polyethylene as artificial joint materials

Ultra-low-wear polyethylene (ULWPE) is a new metallocene catalyzed high density polyethylene (HDPE)material. Previous studies have demonstrated that it has excellent biocompatibility and wear resistance, whereupon indicating great potential in the applications to artificial joints. However, as a newly developed material, its tribological behavior and wear resistance mechanism has not been well understood. In the current study, we experimentally evaluated the tribological behavior of ULWPE, and investigated its high wear resistance mechanism in terms of microstructure, crystallization properties, mechanical, physical, and chemical properties. ULWPE manifested the best tribological performance on pin-on-disc (POD) wear tests compared with the most widely used artificial joints materials, with a wear volume of 0.720 ± 0.032 mm³/million cycles (Mc) and 0.600 ± 0.027 mm³/Mc against cobalt-chromium (CoCr) alloy disc and zirconia toughened alumina (ZTA) ceramic disc, respectively. The results of the wear morphology analysis showed that the surface of ULWPE was the slightest, with no obvious surface damage, debris shedding and wear pits. We reveal that three major factors mainly contributed to its high wear resistance. First, ULWPE demonstrated a high crystallinity and a compact crystalline morphology comprised of long linear molecular chains, which contributed to its good mechanical performance. As confirmed by the mechanical test, ULWPE had a very high density, hardness, and tensile elongation at break. The high hardness and strength laid a solid foundation to a low wear volume, and its high ductility and hardness helped to endure abrasive and adhesive wear, resulting in excellent wear resistance. Second, the results of wettability analysis showed that the contact angle formed on the surface of ULWPE was the lowest and the surface energy was the highest. The hydrophilicity of ULWPE provided good lubrication conditions in body fluid. Third, it also had a lower oxidation index. The high hardness, high strength, high ductility and good wetting of ULWPE materials reduced the damage of the material to adhesion and abrasive wear, resulting in excellent wear resistance.