Stability of screw-retention in two-piece zirconia implants: An in vitro study

To compare the stability of a screw-retained connection in a novel two-piece zirconia implant to a conventional titanium-based connection in an in vitro chewing simulation including artificial ageing.

Incisor (I) and molar (M) shaped monolithic zirconia crowns were screw-retained on either two-piece zirconia (test) or two-piece titanium (control) implants resulting in 4 groups of 8 samples (titanium implants with incisor-shaped crowns (T-I), titanium implants with molar-shaped crowns (T-M), zirconia implants with incisor-shaped crowns (Z-I) and zirconia implants with molar-shaped crowns (Z-M). These were subjected to artificial ageing by thermal cycling (TC: 2 × 3000 × 5°C/55°C cycles of 2 min) and mechanical loading (ML: 1.2 × 10⁶ cycles of 50 N, f = 1 Hz). Surviving samples additionally underwent a fracture force test. Kaplan-Meier plots were drawn, and two-way ANOVA was calculated taking anatomical localisation and material variables as factors.

The mean corresponding survival times were lower for T-M (0.86 × 10⁶  ± 0.31 × 10⁶ cycles) and Z-I (0.84 × 10⁶  ± 0.21 × 10⁶ cycles) compared to T-I (1.14 × 10⁶  ± 0.10 × 10⁶ cycles) and Z-M (1.20 × 10⁶  ± 0.10 × 10⁶ cycles). In one-way ANOVAs for survival time dependent on either location or material, no statistically significant differences could be found (location: p = .31; material: p = .62) in one-way ANOVAs. The interaction of location and material showed significant differences (F = 21.3, p < .001).

The connection of the tested screw-retained zirconia crowns in two-piece zirconia implants is comparable to standard titanium implants in the specific in vitro testing.