Influence of Polyol/Crosslinker Blend Composition on Phase Separation and Thermo-Mechanical Properties of

Said Arévalo-Alquichire1,2, Maria Morales-Gonzalez1, Kelly Navas-Gómez1

  • 1Energy, Materials and Environmental Group, GEMA, Faculty of engineering, Universidad de La Sabana, 140013 Chía, Cundinamarca, Colombia.

Polymers
|March 21, 2020
PubMed

Keywords:
crosslinkerphase separationpolyolpolyurethanethermo-mechanical properties

More Related Videos

Thin Film Composite Silicon Elastomers for Cell Culture and Skin Applications: Manufacturing and Characterization08:02

Thin Film Composite Silicon Elastomers for Cell Culture and Skin Applications: Manufacturing and Characterization

Published on: July 3, 2018

11.0K
Stabilizing Hepatocellular Phenotype Using Optimized Synthetic Surfaces08:50

Stabilizing Hepatocellular Phenotype Using Optimized Synthetic Surfaces

Published on: September 26, 2014

10.5K

Related Concept Videos

Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
2.7K
Polymer Classification: Architecture01:14

Polymer Classification: Architecture

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
3.6K
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
3.7K
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
3.1K