Magnetic quantification of single-crystalline Fe and Co nanowires via off-axis electron holography

Investigating the local micromagnetic structure of ferromagnetic nanowires (NWs) at the nanoscale is essential to study the structure-property relationships and can facilitate the design of nanostructures for technology applications. Herein, we synthesized high-quality iron and cobalt NWs and investigated the magnetic properties of these NWs using off-axis electron holography. The Fe NWs are about 100 nm in width and a few micrometers in length with a preferential growth direction of [100], while the Co NWs have a higher aspect-ratio with preferential crystal growth along the [110] direction. It is noted that compact passivation surface layers of oxides protect these NWs from further oxidation, even after nearly two years of exposure to ambient conditions; furthermore, these NWs display homogeneous ferromagnetism along their axial direction revealing the domination of shape anisotropy on magnetic behavior. Importantly, the average value of magnetic induction strengths of Fe NWs (2.07 {±} 0.10 T) and Co NWs (1.83 {±} 0.15 T) is measured to be very close to the respective theoretical value, and it shows that the surface oxide layers do not affect the magnetic moments in NWs. Our results provide a useful synthesis approach for the fabrication of single-crystalline, defect-free metal NWs and give insight into the micromagnetic properties in ferromagnetic NWs based on the transmission electron microscopy measurements.