Published on: March 13, 2017
Development of a Flex and Stretchy Conductive Cotton Fabric Via Flat Screen Printing of PEDOT:PSS/PDMS Conductive
Granch Berhe Tseghai1,2,3, Benny Malengier1, Kinde Anlay Fante3
1Department of Materials, Textiles and Chemical Engineering, Ghent University, 9000 Gent, Belgium.
Abstract:
In this work, we have successfully produced a conductive and stretchable knitted cotton fabric by screen printing of poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) and poly(dimethylsiloxane-b-ethylene oxide)(PDMS-b-PEO) conductive polymer composite. It was observed that the mechanical and electrical properties highly depend on the proportion of the polymers, which opens a new window to produce PEDOT:PSS-based conductive fabric with distinctive properties for different application areas. The bending length analysis proved that the flexural rigidity was lower with higher PDMS-b-PEO to PEDOT:PSS ratio while tensile strength was increased. The SEM test showed that the smoothness of the fabric was better when PDMS-b-PEO is added compared to PEDOT:PSS alone. Fabrics with electrical resistance from 24.8 to 90.8 kΩ/sq have been obtained by varying the PDMS-b-PEO to PEDOT:PSS ratio. Moreover, the resistance increased with extension and washing. However, the change in surface resistance drops linearly at higher PDMS-b-PEO to PEDOT:PSS ratio. The conductive fabrics were used to construct textile-based strain, moisture and biopotential sensors depending upon their respective surface resistance.