High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia YSZ Scaffolds by In Situ Carbon Templating Xerogels
Published on: April 16, 2017
Structural, chemical and optical characterizations of an experimental SiO2-Y-TZP ceramic produced by the
Victor Mosquim1, Brunna Mota Ferrairo2, Mariele Vertuan1
1Department of Operative Dentistry, Endodontics and Dental Materials, Bauru School of Dentistry, University of São Paulo, Bauru, SP, Brazil.
Abstract:
This study aimed to produce a new SiO2+Y-TZP ceramic via uniaxial/isostatic compression that was structurally and chemically characterized relating to its translucency and flexural strength. SiO2 and Y-TZP were mixed using a ball mill, pressed and sintered at 1150 °C. The optical and mechanical properties of the specimens were compared to lithium disilicate (LD) and zirconia-reinforced lithium silicate (ZLS) (Kruskal-Wallis, α = 0.05). The Fourier Transform Infrared Spectroscopy bands suggested an interaction between Si, O and Zr. Contrast ratio and translucency parameter of the experimental ceramic were higher and lower, (p = 0.000001) respectively, than those of the LD and ZLS. The experimental ceramic presented similar flexural strength to ZLS, but lower than LD (p < 0.0001). It can be concluded that this processing method is efficient to obtain a SiO2+Y-TZP ceramic and 1150 °C crystallizes SiO2 without inducing t-m transformation. The SiO2+Y-TZP ceramic presented lower translucency and higher masking ability than the commercially available glass-ceramics, but similar flexural strength to one glass-ceramics.