Highly Efficient Removal of Cr(VI) from Aqueous Solutions by Polypyrrole/Monodisperse Latex Spheres
Linlin Du1, Peng Gao1, Yide Meng1
1Guangxi Key Laboratory of Optical and Electronic Materials and Devices, College of Materials Science and Engineering, Guilin University of Technology, Guilin 541004, China.
Abstract:
Pyrrole (Py) is easily agglomerated during the polymerization process, affecting its performance. In this paper, polypyrrole/monodispersed latex sphere (PPy/MLS) composites were prepared using in-situ polymerization for the adsorption of hexavalent chromium (Cr(VI)). The specific surface area of PPy/MLS (39.30 m2/g) was increased relative to that of PPy (24.82 m2/g), thus providing more effective adsorption sites. In addition, the adsorption properties of Cr(VI) under different conditions, including Py content, pH of the aqueous solution, and PPy/MLS dosage, were investigated to reveal the adsorption mechanism. The results showed that PPy/MLS possessed high Cr(VI) adsorption capacities when the Py content was 50 wt %. The maximum adsorption capacity was 343.64 mg/g at pH 2.0 and 25 °C. Remarkably, the adsorbents exhibited an excellent removal rate of Cr(VI) after three cycles of adsorption-desorption (over 99%), suggesting that the adsorbents had exceptional recyclability. Furthermore, the adsorption process followed quasi-second-order kinetics and Langmuir isothermal adsorption model. The high adsorption performance, sustainability, and cost-efficiency make this adsorbent a promising candidate for large-scale Cr(VI) contaminant removal.