Influence of pore structure on humidity parameters of cement-polymer mortars contaminated with filamentous fungi

Elżbieta Stanaszek-Tomal1

  • 1Chair of Building Materials Engineering, Faculty of Civil Engineering, PK Cracow University of Technology, Cracow, Poland.

Plos One
|April 10, 2020
PubMed

More Related Videos

Production and Testing of Moisture Behavior and Thermal Properties of Rapeseed Straw and Ganoderma resinaceum Mycelium Bio-Composites09:39

Production and Testing of Moisture Behavior and Thermal Properties of Rapeseed Straw and Ganoderma resinaceum Mycelium Bio-Composites

Published on: September 5, 2025

414
Sandy Soil Improvement through Microbially Induced Calcite Precipitation MICP by Immersion06:27

Sandy Soil Improvement through Microbially Induced Calcite Precipitation MICP by Immersion

Published on: September 12, 2019

9.9K

Related Concept Videos

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
390
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...
356
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
352
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
673
Porosity and Absorption of Aggregate01:20

Porosity and Absorption of Aggregate

Aggregates contain pores of varying sizes; while some are completely enclosed within the particles, others open onto the surface, allowing water to penetrate. The porosity of aggregates is a major factor contributing to the overall porosity of concrete, given that aggregates constitute about three-quarters of concrete's volume.
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the...
652
Total Voids in Concrete01:12

Total Voids in Concrete

Total voids in concrete encompass gel water volume, capillary pores, and entrapped air. Gel water (retained within the cement hydration products) and physically entrapped or adsorbed water are significant for the hydration process. For complete hydration, it's estimated that the space needed for the products of a cubic centimeter of cement doubles. Capillary pores constitute the unoccupied space within the hydrated cement paste, with their size largely influenced by the water-to-cement...