Production and Characterization of Large-Scale Recycled Newspaper Enhanced HDPE Composite Laminates

Recycled newspaper (NP)/high density polyethylene (HDPE) laminated composite can reach the physical and mechanical criteria for most industrial applications, which shows the potential of using solid-state waste paper in engineering materials. Herein, the effects of splicing pattern and size on the physical and mechanical properties of the laminated composite were investigated with the ultimate purpose to fabricate a large-scaleale composite. The laminated composite with a stair-like splicing had better physical and mechanical properties than that with a vertical splicing. An efficient stress transfer could be guaranteed when the distance between the two adjacent junctions were greater than a critical proportion of 1/32 of the length at longitudinal direction. The tensile and flexural properties of the large-scaleale composite with a stair-like splicing, which was fabricated at the splicing ratio of 1/32, were 109 ± 4.2 MPa (MOR), 9836 ± 411 MPa (MOE), 119 ± 7.1 MPa (MOR) and 10002 MPa ± 347 (MOE).