Surface dissolution and transesterification of thermoset dimethacrylate polymer by dimethacrylate adhesive resin and
Santhosh Basavarajappa1, Leila Perea-Lowery2, Abdullah Maghram Alshehri1
1Dental Biomaterial Research Chair, Dental Health Department, College of Applied Medical Sciences, King Saud University, Riyadh 11433, Saudi Arabia.
Objectives:
To evaluate transesterification based dissolution of dimethacrylate and epoxy polymers, the former containing ester groups. Polymer substrates were treated with an adhesive resin (Stick™ Resin) and an organic catalyst-alcohol solution (ethylene glycol and triazabicyclodecene). The surface was chemically and nanomechanically analyzed with Fourier Transform-Infrared (FTIR) spectroscopy, surface profile peak (Rp) and nanohardness and modulus of elasticity.
Methods:
A total of 100 specimens each of light-cured dimethacrylate polymer and heat-cured diepoxy polymer were prepared. 20 specimens were randomly selected and used as control group (0s). The remaining specimens were randomly divided into 40 each for treatment with an Stick™ resin and ethylene glycol+triazabicyclodecene. Within each group the 40 specimens were randomly subdivided into 20 each for treatment at 5min and 24h, with 10 specimens for FTIR and nanohardness and modulus of elasticity, and the other 10 for SEM and surface Rp analyses.
Results:
Dimethacrylate polymer showed a reduction in the nanohardness and modulus of elasticity, Rp values and SEM also showed significant topographical changes after being treated with either Stick™ resin or ethylene glycol+triazabicyclodecene, whereas epoxy resin substrate did not. FTIR analyses affirmed changes in the intensity of ester groups.
Significance:
Ester group containing dimethacrylate polymer showed a reduction in NMP within 5min of exposure to the treatment agents with softening by solution ethylene glycol+triazabicyclodecene associated to the reduction of ester groups in the polymer structure by transesterification. Epoxy polymer without ester groups was not affected by surface softening with treatment agents. Adhesive resin caused surface swelling.
Related Concept Videos
00:53Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)
Similar to cross-metathesis, ADMET also involves the formation of metallacyclobutane intermediate by [2+2] cycloaddition of one of the double bonds of a terminal diene with...
01:13Olefin Metathesis Polymerization: Overview
Ruthenium-based Grubbs catalyst is the most commonly used catalyst for olefin metathesis polymerization. Grubbs catalyst consists of a...
01:33Carboxylic Acids to Methylesters: Alkylation using Diazomethane
02:35Ethers from Alkenes: Alcohol Addition and Alkoxymercuration-Demercuration
Ethers can also be prepared from alkenes through acid-catalyzed addition of alcohols and alkoxymercuration–demercuration.
Preparation of Ethers by Acid-Catalyzed Addition of Alcohol to Alkenes
The acid-catalyzed addition of alcohol to an alkene involves treating the alkene with an excess of alcohol in the presence of an acid catalyst to form an ether under suitable conditions. The hydrogen will add to the less substituted carbon so that the nucleophile can attack the more substituted...
01:20Types of Step-Growth Polymers: Polyesters
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the polymer...
02:29Ethers from Alcohols: Alcohol Dehydration and Williamson Ether Synthesis
Ethers can be prepared from organic compounds by various methods. Some of them are discussed below,
Preparation of Ethers by Alcohol Dehydration
In this method, in the presence of protic acids, alcohol dehydrates to produce alkenes and ethers under different conditions. For example, in the presence of sulphuric acid, dehydration of ethanol at 413 K yields ethoxyethane, whereas it yields ethene at 443 K.