Bio-assisted synthesized Pd nanoparticles supported on ionic liquid decorated magnetic halloysite: an efficient...

Using natural materials, i.e. halloysite nanoclay that is a biocompatible naturally occurring clay and Heracleum persicum extract that can serve as a green reducing agent, a novel magnetic catalyst, Fe₃O₄/Hal-Mel-TEA(IL)-Pd, has been designed and fabricated. To prepare the catalyst, halloysite was first magnetized (magnetic particles with mean diameter of 13.06 ± 3.1 nm) and then surface functionalized with melamine, 1,4 dibromobutane and triethanolamine to provide ionic liquid on the halloysite surface (5 wt%). The latter was then used as a support to immobilize Pd nanoparticles that were reduced by Heracleum persicum extract. The characterization of the catalyst established that the loading of Pd in Fe₃O₄/Hal-Mel-TEA(IL)-Pd was very low (0.93 wt%) and its specific surface area was 63 m²g^-1. Moreover, the catalyst showed magnetic property (Ms = 19.75 emu g^-1) and could be magnetically separated from the reaction. The catalytic performance of the magnetic catalyst for reductive degradation of methyl orange and rhodamine B in the presence of NaBH₄ in aqueous media was investigated. The activation energy, enthalpy, and entropy for the reduction of methyl orange were estimated as 42.02 kJ mol^-1, 39.40 kJ mol^-1, and -139.06 J mol^-1 K^-1, respectively. These values for rhodamine B were calculated as 39.97 kJ mol^-1, 34.33 kJ mol^-1, and -155.18 Jmol^-1K^-1, respectively. Notably, Fe₃O₄/Hal-Mel-TEA(IL)-Pd could be reused for eight reaction runs with negligible loss of the catalytic activity (~3%) and Pd leaching (0.01 wt% of the initial loading).