Type-II GaSb quantum dots grown on InAlAs/InP (001) by droplet epitaxy
Qing Yuan1, Baolai Liang1,2, Shiping Luo1
1Hebei Key Laboratory of Optic-electronic Information and Materials, College of Physics Science & Technology, Hebei University, Baoding 071002, People's Republic of China.
Abstract:
GaSb quantum dots (QDs) have been grown by droplet epitaxy within InAlAs barrier layers on an InP (001) substrate. The droplet growth mode facilitates a larger size (average height ∼4.5 nm) and a lower density (∼6.3 × 109 cm-2) for the QDs than would be expected for the 4% lattice mismatch between GaSb and InAlAs. A type-II band alignment between the GaSb QDs and the InAlAs barriers is revealed by photoluminescence (PL) through a prominent blue-shift of ∼0.11 eV resulting from a six orders of magnitude increase in excitation power. Further confirmation of the type-II nature of these QDs is found through time-resolved PL studies showing a biexponential decay with a long carrier lifetime of ∼10.9 ns. These observations reveal new information for understanding the formation and properties of GaSb/InAlAs/InP QDs, which may be an optimum system for the development of both efficient memory cells and photovoltaic devices.