A Study for Improving Compressive Strength of Cementitious Mortar Utilizing Magnetic Water

Omar M M Yousry1, Metwally A Abdallah1, Mariam F Ghazy1

  • 1Structural Engineering Department, Tanta University, Tanta 31733, Egypt.

Materials (Basel, Switzerland)
|April 29, 2020
PubMed

Keywords:
cementitious mortarcompressive strengthfly ashmagnetic watermortar flowsuperplasticizer

More Related Videos

Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes09:41

Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes

Published on: May 17, 2018

13.9K
Sandy Soil Improvement through Microbially Induced Calcite Precipitation MICP by Immersion06:27

Sandy Soil Improvement through Microbially Induced Calcite Precipitation MICP by Immersion

Published on: September 12, 2019

9.9K

Related Concept Videos

Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
385
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
340
Testing Water Quality01:14

Testing Water Quality

When the quality of water for concrete preparation is uncertain, its impact on the setting time of cement and compressive strength of mortar is assessed by comparison with de-ionized or distilled water benchmarks. American Society for Testing and Materials (ASTM) C1602 requires the setting times to be within 90 minutes of the control, British Standard (BS) 3146:1980 allows a 30-minute variance in the initial setting, while British Standards European Norm (BS EN) 1008 specifies initial setting...
301
Mortar01:29

Mortar

Mortar, a mixture of Portland cement, hydrated lime, sand, and water, is a crucial binding material in construction. Its primary function is to join masonry units together, filling gaps and ensuring a uniform distribution of weight across the structure. This helps in preventing potential weaknesses. Mortar also serves as a protective barrier against environmental elements such as water and wind, thereby safeguarding the interior of the structure. It also compensates for surface irregularities...
464
Water Cement Ratio01:28

Water Cement Ratio

The water-cement ratio is pivotal in defining concrete's quality. This ratio, a balance between the weight of water and cement in the mix, shapes the concrete's strength, durability, and resistance to environmental factors. As identified by Abrams’ law, less water in the mix equates to stronger concrete. However, water is essential not only for the chemical process of hydration but also for the concrete's workability and compaction. While hydration chemically binds water and...
992
Effect of Sea Water on Concrete01:22

Effect of Sea Water on Concrete

Concrete exposed to seawater can undergo degradation like the dissolution of ettringite and gypsum, increasing the material's porosity and decreasing its strength. In contrast, the crystallization of salts within the concrete's pores can cause expansion, particularly above the waterline where evaporation occurs. Nonetheless, this expansion only happens when seawater, enabled by the concrete's permeability, manages to infiltrate the structure.