The Effects of Adding Different HALS on the Curing Process, Film Properties and Lightfastness of Refined Oriental...

Oriental lacquer is a natural polymeric coating with a satiny texture and excellent characteristics, such as chemical resistance and durability. However, the poor lightfastness resulted in the natural aromatic structures of the urushiol structures limited its suitability for outdoor application. This study aimed at the improvement of the lightfastness by adding the different hindered amine light stafbilizers (HALS) with 2 phr addition as well as the effects on the coating and film property of the refined oriental lacquers (RL). The Cryptomeria japonica plate, glass sheets, and the other substrates were used for finishing. The results showed that the lightfastness of RL film was obviously improved by adding 2 phr HALS of Bis(2,2,6,6-tetramethyl-4-piperidinyl) sebacate (H90) containing -NH group and Bis (1,2,2,6,6-pentamethyl-4-piperidinyl)-[[3,5-bis(1,1-dimethyl ethyl) -4-hydroxyphenyl] methyl] butylmalonate (H60) containing -NCH₃ groups. The HALS additions increased the pH value of RL and improved the activities of laccase-catalyzed reaction. Meanwhile, the oxidative polymerization of the side chains of RL was inhibited, caused by a radical scavenging ability of HALS. The changes in the drying process affected not only the curing time, but also the film properties. Among the 2 phr additions of different HALS, the film containing H90 had the best lightfastness. Meanwhile, it kept the most similar properties with RL and shortened the drying time of RL, and it was selected as the best HALS addition under 2 phr in this study.