Efficient Gas Barrier and Antibacterial Properties of Poly(lactic acid) Nanocomposites: Functionalization with Phytic...

Poly(lactic acid) (PLA) represents one of the most promising and attractive bio-based polymers for green packaging. However, toughness, gas barrier and antibacterial properties of pure PLA films cannot compete with those of traditional petroleum-based active packaging plastics. To fill this gap, utilization of excellent chelating properties of phytic acid (PA), functionalized layered double hydroxides (LDHs@PA-Cu(II)) was firstly synthetized via facile deposition and chelation of one-step assembled PA-Cu(II) coordination compounds on the surface of layered clay. Furthermore, LDHs@PA-Cu(II)/PLA nanocomposites were prepared by blending LDHs@PA-Cu(II) and pure PLA via solution casting evaporation process. After adding only 1 wt % LDHs@PA-Cu(II), elongation at break and tensile strength increase by 53.0% and 18.9%, respectively, and the oxygen relative permeability decreases by 28.0%. Due to the strong interface interaction and heterogenous nucleation, the reinforcement effect of LDHs@PA-Cu(II) at low loadings is remarkable. Meanwhile, owing to the antibacterial activity of PA-Cu(II) coatings, the antibacterial rate (against Escherichia coli) of LDHs@PA-Cu(II) exceeds 99.99%. Furthermore, the corresponding LDHs@PA-Cu(II)/PLA nanocomposites also show outstanding antibacterial properties, which will be a promising candidate for active packaging application.