Relationship between the Ionization Degree and the Inter-Polymeric Aggregation of the Poly(maleic...

Alternating amphiphilic copolymers are macromolecular systems with a polarity duality in their structure, since they are generally formed by alternating segments corresponding to a potential electrolyte group and an alkyl (aliphatic or aromatic) group. These systems, depending on the ionization degree, as well as the time, may form different types of intra and interpolymeric aggregates in aqueous media. Therefore, this study, which in fact is the continuation of a previously reported work, is focused on establishing how the ionization degree of the sodium and potassium salts of the poly(maleic acid-alt-octadecene) affect zeta potential, pH, electrical conductivity, particle size, polydispersity index, and surface tension over time. The results showed that polymeric salts with a high ionization degree in aqueous media formed homogeneous systems with bimodal sizes and high zeta potential values, which tended to quickly become less negative, lowering the pH and slightly increasing the electrical conductivity; while systems with low ionization degree lead to the opposite, forming heterodispersed systems with several populations of particle sizes, high polydispersity, low zeta potential values, neutral and invariable pH values, and high electrical conductivity values. Consequently, these results suggest that the values of particle size, polydispersity index, zeta potential, pH, and electrical conductivity change regarding the polymeric ionization degree, as well as the time. Therefore, such variables should be considered and controlled when working with this kind of polymeric materials.