Ultrasound assisted deposition of highly stable self-assembled Bi₂MoO₆ nanoplates with selective crystal facet...

The use of crystal facets of photocatalysts is well known as a promising strategy for the design of new photocatalysts with interesting physicochemical features for energy production applications. In this work, Bi₂MoO₆ thin films were synthesized by two methods, electrodeposition and sonoelectrodeposition. Preferential growth orientation depended on synthesis method. Results suggested that sonoelectrodeposition led to dominate the crystal facet {1 0 0} growth with self-assembled nanoplate morphologies while growth orientation in the {0 1 0} facet was dominant in electrodeposition in the absence of ultrasonic waves. As a highlight result, the {1 0 0} facet shows a smaller band gap, higher photocatalytic water splitting than the {0 1 0} facet. Efficient separation of charge pairs and long life time of photogenerated electrons was observed to be intrinsic features of the {1 0 0} facets. The higher charge transfer was confirmed by a higher photocurrent from linear sweep voltammetry and a smaller Nyquist radius arc. Ultrasound plays a key role in growth orientation and led to a production of homogeneous films with nanoplates which self-assembled together to form a flower-like structure. While in the absence of ultrasound the film has coral-like structure. Highly stable sonoelectrodeposited films exhibited incident photon-to-electron conversion efficiency (IPCE) of 22.4% at the specific wavelength of 500 nm. The sonoelectrodeposition method could act as a promising method for forming new films with specific crystal facet selection and developing as highly efficient photoanodes for PEC water splitting.