Enhanced Photoelectrochemical Water Oxidation from CdTe Photoanodes Annealed with CdCl₂

Most CdTe photoanodes and photocathodes show positive and negative photocurrent onset potentials for water oxidation and reduction, respectively, and are thus unable to drive photoelectrochemical (PEC) water splitting without external applied biases. Herein, the activity of a CdTe photoanode having an internal p-n junction during PEC water oxidation was enhanced by applying a CdCl₂ annealing treatment together with surface modifications. The resulting CdTe photoanode generated photocurrents of 1.8 and 5.4 mA cm^-2 at 0.6 and 1.2 V_RHE , respectively, with a photoanodic current onset potential of 0.22 V_RHE under simulated sunlight (AM 1.5G). The CdCl₂ annealing increased the grain sizes and lowered the density of grain boundaries, allowing more efficient charge separation. Consequently, a two-electrode tandem PEC cell comprising a CdTe-based photoanode and photocathode split water without any external bias at a solar-to-hydrogen conversion efficiency of 0.51 % at the beginning of the reaction.