Magnetoimpedance spectroscopy of phase-separated La_0.5Ca_0.5MnO₃ polycrystalline manganites

Magnetoimpedance spectroscopy was carried out on phase-separated La_0.5Ca_0.5MnO₃ polycrystalline manganites. The La_0.5Ca_0.5MnO₃ powder was synthesized following an adapted sol-gel route. Structural and magnetic data showed the signs of phase coexistence of ferromagnetic (FM) Pnma and charge-ordered antiferromagnetic (CO-AFM) P2₁/m phases. Magnetization vs. temperature (M vs. T) measurements revealed several magnetic transitions from the high temperature paramagnetic (PM) to an FM phase upon cooling (PM-FM) at ≈240 K, FM-AFM (≈170 K) and AFM-FM (≈100 K). Magnetic field (H)-dependent impedance spectroscopy data were collected from sintered pellets and fitted with an equivalent circuit model to separately analyze the different dielectric contributions from the grain boundary (GB) and the grain interior bulk areas. This allowed separating the GB and bulk magnetoresistance (MR), which was shown to amount to a maximum of ≈80% for both GB and bulk at H = 10 T near the metal-insulator transition (MIT) at ≈100 K. The GB resistance was found to be larger than the bulk resistance by a factor of ≈3, which implies that the direct current (DC) resistance and DC MR are dominated by contributions from the GBs. The magnetocapacitance (MC) effects detected were all found to be small below ≈3%, including in the presence of a CO phase.