Electrospun poly(3-hydroxybutyrate-co-4-hydroxybutyrate) /Octacalcium phosphate Nanofibrous membranes for effective
Zetao Wang1, Ke Ma2, Xianfang Jiang3
1Guangxi Engineering Center in Biomedical Materials for Tissue and Organ Regeneration & Guangxi Collaborative Innovation Center for Biomedicine, Life Sciences Institute, Guangxi Medical University, Nanning, 530021, China; Pharmaceutical college, Guangxi Medical University, Nanning, 530021, China.
Abstract:
Membranes used in guided bone regeneration (GBR) are required to exhibit high mechanical strength, biocompatibility, biodegradation, osteogenic and osteoinductive potential. In our study, poly(3-hydroxybutyrate-co-4-hydroxybutyrate)(P(3HB-co-4HB))/octacalcium phosphate (OCP) (P(3HB-co-4HB)/OCP) nanofibrous membranes were fabricated by electrospinning with two different P(3HB-co-4HB) to OCP ratios (P(3HB-co-4HB):OCP = 95:5 wt% and 90:10 wt%, termed P(3HB-co-4HB)/OCP(5)and P(3HB-co-4HB)/OCP (10), respectively) for GBR. The developed P(3HB-co-4HB)/OCP nanofibrous membranes were analysed for their osteogenic and osteoinductive properties using mesenchymal stem cells (MSCs) in vitro and in a calvarial bone defect rat model. The composite P(3HB-co-4HB)/OCP nanofibrous membranes showed decreased fibre size and enhanced tensile strength compared with those of P(3HB-co-4HB) nanofibrous membranes. In the in vitro studies, the P(3HB-co-4HB)/OCP membranes facilitated cell growth and osteoblastic differentiation of MSCs and were superior to P(3HB-co-4HB) membranes. After covered on the calvarial bone defects, P(3HB-co-4HB)/OCP membranes facilitated greater neobone formation than P(3HB-co-4HB) membranes did, as the result of histological evaluation and micro-CT analysis with higher bone volume/total volume (BV/TV) ratio and bone mineral density (BMD). P(3HB-co-4HB)/OCP(10) membranes with higher OCP content showed greater stiffness and osteoinductivity than P(3HB-co-4HB)/OCP (5)membranes, demonstrating the role of OCP in the composite membranes. These results indicated that electrospun P(3HB-co-4HB)/OCP nanofibrous membranes hold promise for the clinical application of GBR.