Synthesis of the perovskite-type oxyfluoride AgTiO₂F: an approach adopting the HSAB principle

A synthetic approach for oxyfluorides involving the hard and soft acids and bases (HSAB) principle was examined. Using AgF composed of the Ag+ ion as a soft acid and F- as a hard base, we attempted to synthesize an oxyfluoride, AgTiO2F, that included the O2- ion as a softer base than the F- ion and the Ti4+ ion as a harder acid than the Ag+ ion. Consequently, a perovskite (Pv)-type oxyfluoride AgTiO2F was synthesized by a solid-state reaction under ambient pressure and under high pressure, and a heat treatment at 1000 °C for 30 min under a pressure of 4 GPa produced the Pv-type phase with minimal impurity phases. The lack of an optical second harmonic generation (SHG) response and the result of Rietveld refinement indicated that the compound is centro-symmetric and shows the anti-phase tilt of Ti(O, F)6 octahedra along the c-axis on the basis of the space group I4/mcm. O/F ordering on the anion site was not clarified. The phase stability of a Pv-type AgTiO2F is discussed in terms of the HSAB principle and the thermodynamics in the formation of the Pv-type phase by comparing KTiO2F and NaTiO2F. AgTiO2F has a light yellow color and a band gap energy of 2.8 eV in the visible region, which originates from the covalent bonding between the soft cation Ag+ and O2- as a softer anion than F-. We propose that the HSAB principle is useful for selecting a cation for the synthesis of oxyfluorides.