Related Experiment Video

Updated: Dec 20, 2025

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

643

Microleakage patterns of glass ionomer cement at cement-band and cement-enamel interfaces in primary teeth

P Shankar1, Ramesh Venkatesan2, D Senthil1

  • 1Department of Paedodontics and Preventive Dentistry, SRM Dental College and Hospital, Ramapuram, Chennai, Tamil Nadu, India.

Indian Journal of Dental Research : Official Publication of Indian Society for Dental Research
|May 22, 2020
PubMed
Abstract

Keywords:
GICRMGICmicroleakage

More Related Videos

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

13.9K
Author Spotlight: Establishing an Accurate Microhardness Testing Protocol for Craniofacial Tissues06:16

Author Spotlight: Establishing an Accurate Microhardness Testing Protocol for Craniofacial Tissues

Published on: April 26, 2024

1.1K

Related Concept Videos

Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
353
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
385
Teeth01:15

Teeth

The formation of teeth, also known as odontogenesis, is a complex process that begins in utero, around the sixth week of embryonic development. There are three stages to this process: the bud stage, the cap stage, and the bell stage.
In the bud stage, the tooth germ (an aggregation of cells) starts to form in the developing jawbone. During the cap stage, the tooth germ differentiates into enamel organ, dental papilla, and dental sac, which will later develop into the tooth's enamel, dentin...
1.5K
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...
347
Bleeding in Fresh Concrete01:22

Bleeding in Fresh Concrete

Bleeding in fresh concrete occurs when water from the mix rises to the surface. This happens because the mix's solid components fail to retain all the water as they settle, leading to separation where water collects at the top. The severity of bleeding can be measured by assessing the total settlement or by noting the decrease in height per unit height of concrete.
Bleeding can cause several issues in the concrete structure. Sometimes, the rising water gets trapped beneath large aggregate...
422