Effect of Different Phosphate Glass Compositions on the Process-Induced Macromolecular Dynamics of Polyamide 66

The present study provides a fundamental understanding of the mechanism of action of special new phosphate glass (P-glass) systems, having different glass transition temperatures (T_g), in polyamide 66 (PA66). Dynamic mechanical analysis (DMA) revealed that the T_g of PA66/low T_g P-glass (ILT-1) was significantly shifted to a lower T_g (65 °C), and another transition appeared at high temperature (166 °C). This was supported by a drop in the melting point and the crystallinity of the PA66/ILT-1 hybrid material as detected by differential scanning calorimetry (DSC). The dielectric spectroscopic investigation on the networks' molecular level structural variations (T_g and sub-T_g relaxations) agreed very well with the DMA and DSC findings. Contrary to intermediate T_g(IIT-3) and high T_g P-glass (IHT-1) based materials, the PA66/ILT-1 hybrid material showed an evidence of splitting the PA66 T_g relaxations into two peaks, thus confirming a strong interaction between PA66 and ILT-1 (low T_g P-glass). Nevertheless, the three different P-glass compositions did not show any effect on the PA66 sub-T_g relaxations (related to the -NH₂ and -OH chain end groups' motion).