Influence of Phosphorus Slag on Physical and Mechanical Properties of Cement Mortars

Influences of phosphorus slag from 10% to 50% (by mass) on the setting time and the water requirement of the normal consistency of cement pastes, flowability, resistance to carbonation, and the compressive strength of cement mortars were investigated. The physical activation by improving fineness and the chemical activation by adding the chemical activator were evaluated by the compressive strength of cement mortars with 30% by mass of phosphorus slag. Hydration heat, X-ray diffraction, and scanning electron microscopy were used to study the microstructure of cement pastes and mortars with 30% by mass of phosphorus slag and the chemical activator. Results showed that the setting time of cement pastes was delayed by phosphorus slag from 10% to 50%. Phosphorus slag had nearly no effects on the water requirement of the normal consistency of cement pastes and the flowability of cement mortars. The resistance to carbonation of cement mortars was decreased by phosphorus slag from 10% to 50% according to the acceleration carbonation. The compressive strength of cement mortars was also decreased by phosphorus slag from 10% to 50% and the low activity of phosphorus slag was concluded based on compressive strength of cement mortars. The effect of the chemical activator on the compressive strength of cement mortars with 30% by mass of phosphorus slag was better than improving fineness of phosphorus slag from 300 m²/kg to 450 m²/kg. Both hydration heat and cement hydrates were inhibited by phosphorus slag and could be partly compensated by the chemical activator. Loose morphology and propagations of microcracks were found in cement pastes and mortars with 30% by mass of phosphorus slag.