Synthesis and Characterization of Novel Nanoporous Gl-POSS-Branched Polymeric Gas Separation Membranes

Novel nanoporous Gl-POSS-branched polymers based on the macroinitiator of anionic nature, 2,4-toluene diisocyanate, and octaglycidyl polyhedral oligomeric silsesquioxane (Gl-POSS) were obtained as gas separation membranes. The synthesis of polymers was carried out using various loads of Gl-POSS. It was found that the main reaction proceeding with 2,4-toluene diisocyanate is the polyaddition, accompanied by the isocyanate groups opening of the carbonyl part. This unusual opening of isocyanate groups leads to the formation of coplanar acetal nature polyisocyanates (O-polyisocyanate). The terminal O-polyisocyanate links initiate the subsequent opening of the epoxide rings in Gl-POSS. As a result, Gl-POSS serves as a hard and bulky branching agent and creates the specific framing supramolecular structure, which leads to the formation of nanopores in the polymer, where the flexible polyether components are located inside the cavities. Thermal, mechanical, physical, and chemical properties of the obtained polymers were studied at various Gl-POSS contents in the polymer matrix. It was found that these polymers show high selectivity of gas transport properties for pure ammonia relative to nitrogen and hydrogen at ambient temperature. Measurements showed that the gas permeability coefficients and the values of ideal selectivity were in a non-additive dependence to the Gl-POSS content.