Skeleton-Structure WS₂@CNT Thin-Film Hybrid Electrodes for High-Performance Quasi-Solid-State Flexible...

The purpose of this work is to explore the application prospects of WS₂ as an active material in flexible electrodes. Since WS₂ has similar disadvantages as other two-dimensional layered materials, such as easily stacking, it is essential to develop a three-dimensional structure for its assembly in terms of electrochemical performance. In addition, the low conductivity of WS₂ limits its application as flexible electrode material. In order to solve these problems, carbon nanotubes (CNTs) are introduced to improve the conductivity of hybrid WS₂ materials and to construct a skeleton structure during WS₂ assembly. Compared with pure CNTs and WS₂, the WS₂@CNT thin-film hybrid with a unique skeleton structure has a high specific area capacitance that reaches a maximum of 752.53 mF/cm² at a scan rate 20 mV/s. Meanwhile, this hybrid electrode material shows good stability, with only 1.28% loss of its capacitance over 10,000 cycles. In order to prove its feasibility for practical application, a quasi-solid-state flexible supercapacitor is assembled, and its electrochemical characteristics (the specific area capacitance is 574.65 mF/cm²) and bendability (under bending to 135° 10, 000 times, 23.12% loss at a scan rate of 100 mV/s) are further investigated and prove its potential in this field.