Single versus dual orthogonal plating for comminuted midshaft clavicle fractures: a biomechanics study

Dual orthogonal plating of clavicle fractures may provide greater stiffness and strength than unilateral plate constructs and allow the use of lower-profile plates. We aim to biomechanically compare three clavicle plating constructs in a comminuted clavicle fracture model.

Fifteen clavicle sawbones were osteotomised, simulating a comminuted midshaft fracture and allocated to either: group 1, single superior plate (3.5 mm superior plate); group 2, combination plating (3.5 mm superior plate, 2.8 mm anterior plate) and group 3, dual mini-plates (two 2.8-mm orthogonal mini-plates). Specimens were biomechanically tested under torsion and cantilever bending. Construct stiffness (Nm/degree) and load to failure (Nm) were measured.

Group 2 had higher torsional (0.70 vs. 0.60 Nm/deg, p = 0.017) and cantilever bending stiffness (0.61 vs. 0.51 Nm/deg, p = 0.025) than group 1. Group 3 had lower cantilever bending stiffness (0.39 vs. 0.51 Nm/deg, p < 0.004) and load to failure (40.87 vs. 54.84 Nm, p < 0.01) than group 1. All dual plate constructs that catastrophically failed did so from fracture at the lateral ends of the plates. Single plate constructs failed due to plate bending.

Dual orthogonal fixation with mini-plates demonstrated lower stiffness and strength than traditional superior plating. The addition of an anterior mini-plate to a traditional superior plating improved construct stiffness and may have a role in patients seeking early return to activity.

Basic science biomechanical study.