Biomechanical Analysis of Plate Fixation Compared With Various Screw Configurations for Use in the Latarjet Procedure

The biomechanical properties of coracoid fixation with a miniplate during the Latarjet procedure have not been described.

To determine the biomechanical properties of miniplate fixation for the Latarjet procedure compared with various screw fixation configurations.

Controlled laboratory study.

A total of 8 groups (n = 5 specimens per group) were tested at a screw insertion angle of 0°: (1) 3.75-mm single screw, (2) 3.75-mm double screw, (3) 3.75-mm double screw with washers, (4) 3.75-mm double screw with a miniplate, (5) 4.00-mm single screw, (6) 4.00-mm double screw, (7) 4.00-mm double screw with washers, and (8) 4.00-mm double screw with a miniplate. In addition, similar to groups 1 to 3 and 5 to 7, there were 30 additional specimens (n = 5 per group) tested at a screw insertion angle of 15° (groups 9-14). To maintain specimen uniformity, rigid polyurethane foam blocks were used. Testing parameters included a preload of 214 N for 10 seconds, cyclical loading from 184 to 736 N at 1 Hz for 100 cycles, and failure loading at a rate of 15 mm/min until 10 mm of displacement or specimen failure occurred.

All single-screw constructs and 77% of 15° screw constructs failed before the completion of cyclical loading. Across all groups, group 8 (4.00-mm double screw with miniplate) demonstrated the highest maximum failure load (P < .001). There were no differences in failure loads among specimens with single-screw fixation (groups 1, 5, 9, and 12; P > .05). All specimens in groups 9, 10, 11, 12, 13, and 14 (insertion angle of 15°) had significantly lower maximum failure loads compared with specimens in groups 2, 3, 4, 6, 7, and 8 (insertion angle of 0°) (P < .001 for all).

These results indicate significantly superior failure loads with the miniplate compared with all other constructs. Across all fixation techniques and screw sizes, constructs with screws inserted at 0° performed better than constructs with screws inserted at 15°.

The use of a miniplate for coracoid fixation during the Latarjet procedure may provide a more durable construct for the high-demand contact athlete.