Surface Reconstruction of Ultrathin Palladium Nanosheets during Electrocatalytic CO₂ Reduction

A surface reconstructing phenomenon is discovered on a defect-rich ultrathin Pd nanosheet catalyst for aqueous CO₂ electroreduction. The pristine nanosheets with dominant (111) facet sites are transformed into crumpled sheet-like structures prevalent in electrocatalytically active (100) sites. The reconstruction increases the density of active sites and reduces the CO binding strength on Pd surfaces, remarkably promoting the CO₂ reduction to CO. A high CO Faradaic efficiency of 93 % is achieved with a site-specific activity of 6.6 mA cm^-2 at a moderate overpotential of 590 mV on the reconstructed 50 nm Pd nanosheets. Experimental and theoretical studies suggest the CO intermediate as a key factor driving the structural transformation during CO₂ reduction. This study highlights the dynamic nature of defective metal nanosheets under reaction conditions and suggests new opportunities in surface engineering of 2D metal nanostructures to tune their electrocatalytic performance.