Effect of substrate and cement on the final color of zirconia-based all-ceramic crowns

To evaluate the influence of the substrate and the cement on the final color of ceramic crowns.

Prosthetic crowns (framework + porcelain) were fabricated using two all-ceramic systems (YZ, 3 mol% yttria-stabilized tetragonal zirconia; IZ, alumina-based zirconia-reinforced glass-infiltrated ceramic) and a metal-ceramic system (MC; n = 8). Metal (M) and resin (R) were used as substrate abutments. For R substrate, crowns were evaluated as seated (R) and after cementation (R-C). CIELAB color coordinates were obtained using a dental spectrophotometer with D65 light illumination. CIELAB, CIEDE2000 (1:1:1) and CIEDE2000 (2:1:1) color difference metrics were used. Data were analyzed using 95% confidence intervals and compared to perceptibility (PT) and acceptability (AT) thresholds.

The $$ , ∆E₀₀ (1 : 1 : 1), and ∆E₀₀ (2 : 1 : 1) values of the restorative systems evaluated using different substrates (M.R) were similar to the AT values of each metric. When non-cemented and cemented crowns were evaluated (R.R-C), MC had color difference values at PT and below AT; while YZ and IZ showed similar values to AT, for $$ and ∆E₀₀ (1 : 1 : 1) metrics.

The substrate and cement affected the final color of zirconia-based all-ceramic crowns, but the color differences corresponded to an acceptable match.

As both substrate and cement influence the final color of multi-layered ceramic prosthesis, dentists and dental technicians should understand the optical properties of dental ceramics to reproduce the natural appearance of dental structures and maximize the chance for excellent color matches.