Photocatalytic Efficiency Tuning by the Surface Roughness of TiO₂ Coatings on Glass Prepared by the Doctor Blade...

A set of opaque films were prepared with Degussa P25^® or Hombikat UV100^® TiO₂ powders by the doctor blade method on glass slides with different compositions of polyethylene glycol of 20 kDa (PEG20), and they were characterized by spectroscopy, microscopy and photochemical kinetics measurements. After annealing treatment at 450 °C, about 5-7% C atom was incorporated into the films, as a consequence of the degradation of the organic complexing agents, inducing a small reduction of the energy band gap of TiO₂ (i.e. 3.02 ≤ E_g (eV) ≤ 3.08). All films were about 15 ± 2 μm thick but their micro-morphological characteristics depended on the content of PEG20, showing different patterns of cracks and aggregates that produce intense light scattering and retransmission phenomena with the result of a three-dimensional excitation of the TiO₂ particles in the thick film. Back-face excitation with UVA light (365 ± 42 nm) of the opaque films in contact with an aqueous solution produced both surface-bound and free hydroxyl radicals (HO^• ), as detected using a coumarin solution as a radical dosimeter. The photogeneration efficiency of HO^• decreased with the surface roughness of the films, which varied between 135 and 439 nm depending on the film's composition.