Metal-organic framework derived amorphous VO_x coated Fe₃O₄/C hierarchical nanospindle as anode material for superior...

Lithium-ion batteries (LIBs) are widely regarded as a promising electrochemical energy storage device, due to their high energy density and good cycling stability. To date, the development of anode materials for LIBs is still confronted with many serious problems, and much effort is required for constructing more ideal anode materials. Herein, starting with metal-organic frameworks (MOFs), an amorphous VO_x coated Fe₃O₄/C hierarchical nanospindle has been successfully synthesized. The obtained Fe₃O₄/C@VO_x nanospindle has a uniform particle size of ∼100 nm in diameter and ∼400 nm in length and consists of ultrafine Fe₃O₄ nanoparticles (∼5 nm) embedded in a porous carbon matrix as the core and an amorphous VO_x layer as the shell. Notably, as the anode material for LIBs, Fe₃O₄/C@VO_x delivers a high coulombic efficiency (74.2%) and a large capacity of 845 mA h g^-1 after 500 cycles at 1000 mA g^-1. A prominent discharge reversible capacity of 340 mA h g^-1 is also still retained at 5000 mA g^-1. More importantly, the presented facile MOF-derived route could be easily extended to other functional materials for widespread applications.