Effect of a single-component ceramic conditioner on shear bond strength of precoated brackets to different CAD/CAM...

To compare the shear bond strength (SBS) of the CAD/CAM material-bracket interface using three surface treatments: following manufacturers' instructions (MI), Monobond Etch & Prime (MEP) and 9.6% hydrofluoric acid plus silane (9.6% HF), after 24 h of water storage (24 h) and 10,000 cycles of thermocycling (TC).

A total of 126 crowns with four identical buccal surfaces were fabricated using seven different CAD/CAM materials: CEREC Blocs unglazed (CBU), CEREC Blocs glazed (CBG), IPS Empress CAD (EMP), IPS e.max CAD (EMA), VITA SUPRINITY PC (SUP), inCoris TZI (TZI) and VITA ENAMIC (ENA). A total of 504 APC Flash-Free (APC FF)-precoated brackets were bonded applying three surface treatments: (1) MI; (2) MEP and (3) 9.6% HF. SBS was performed after 24 h and TC. Results were analyzed by Kruskal-Wallis and Mann-Whitney U tests (p < 0.05).

MEP conditioning yielded lower SBS results compared with MI and 9.6% HF for CBG (24 h and TC) and EMA (TC) materials. EMP conditioning with MEP after 24 h obtained lower SBS values compared with MI; however, after TC, SBS was similar to MI group and higher than with 9.6% HF. After TC for TZI ceramic, MI protocol (sandblasting) obtained higher SBS scores than MEP, but similar than 9.6% HF. Treatment of ENA with MI and MEP produced higher results than 9.6% HF after TC. SBS results were similar for CBU and SUP, regardless of the treatment.

Although each CAD/CAM material requires specific surface treatment to obtain the highest SBS of APC FF brackets, the treatment with MEP is a valid orthodontic alternative for most of the materials tested. TC significantly decreased SBS for most of the materials.

MEP can be considered a valid and promising product to condition most of the CAD/CAM ceramics evaluated for APC FF bracket bonding purposes, allowing a faster and safer procedure.