Thickness-Controlled Wafer-Scale Single-Crystalline MAPbBr₃ Films Epitaxially Grown on CsPbBr₃ Substrates by the...

The perovskite single-crystalline thin films, which are free of grain boundaries, would be highly desirable in boosting device performance due to their high carrier mobility, low trap density, and large carrier diffusion length. Herein, a facile room-temperature approach to epitaxially grow MAPbBr₃ single-crystalline films on CsPbBr₃ substrates by the droplet-evaporated crystallization method is reported. A large-area continuous MAPbBr₃ single-crystal film about 15 × 15 mm² in size has been heteroepitaxially grown on CsPbBr₃ substrates. The surface morphology, composition, and single crystallinity were characterized by a scanning electron microscope, an energy-dispersive spectrometer, an electron probe microanalyzer, and high-resolution X-ray diffractions, respectively. The thickness of the films could be adjusted from 1 to 18 μm by varying the concentration of the solution from 10 to 50 wt %. The epitaxial relationship of MAPbBr₃ (010)∥CsPbBr₃ (010), MAPbBr₃ [101]∥CsPbBr₃ [200] was authenticated using XRD, pole figure, and TEM. The low defect density of 4.6 × 10¹¹ cm^-3 and high carrier mobility of 261.94 cm² V^-1 s^-1 of the MAPbBr₃ film measured by the SCLC method are comparable to those of bulk single crystals. An on/off ratio of ∼113 was achieved according to current-voltage curves. Our research demonstrates the first large-area single-crystal heterojunction of a hybrid perovskite with an all-inorganic perovskite, which may show unique properties in optoelectronic applications.