Stable Electrochemical Li Plating/Stripping Behavior by Anchoring MXene Layers on Three-Dimensional Conductive...

The ultrahigh specific capacity of lithium (Li) metal makes it possible to serve as the ultimate candidate for an anode in high-energy density secondary batteries, whereas the safety hazards caused by Li dendrite growth severely hamper the commercialization process of a lithium metal anode. Here, we propose a 3D conductive skeleton by anchoring MXene on Cu foam (MXene@CF) to significantly improve the electrochemical Li plating/stripping behavior. Li metal tends to nucleate uniformly and grow horizontally along the MXene nanosheets under the strong Coulomb interaction between adsorbed Li and MXene. Moreover, the abundant fluorine termination groups in MXene contribute to forming a stable fluorinated solid electrolyte interphase (SEI) and thus effectively regulating the Li deposition behaviors and prolonging the stability of the Li metal anode. Therefore, the MXene@CF skeleton maintains a high Coulombic efficiency (CE) of 98.5% after 200 cycles at 1 mA cm^-2. The MXene@CF-based symmetric cells can run for more than 1000 h without intense voltage fluctuation and demonstrates remarkable deep charge/discharge abilities. The MXene@CF-Li|LiFePO₄ full cell exhibits outstanding long-term cycling stability (95% capacity retention after 300 cycles). Our research suggests that MXene could effectively regulate the Li plating behavior that might provide a feasible solution for a dendrite-free Li anode.