Epoxy Nanocomposites Reinforced with Functionalized Carbon Nanotubes

In this article, amino functionalized multiwalled carbon nanotubes (MWCNTs) were prepared by chemical modification of the surface of a MWCNTs using γ-aminopropyltriethoxysilane (APTES) and dispersed into the epoxy composition. The modifying agent (APTES) was directly deposited on the MWCNTs surfaces. For the functionalization of MWCNTs, was used not the APTES concentrate, as it had been described in previous works, but its freshly prepared aqueous solution. Properties of APTES-treated MWCNTs were characterized by transmission electron microscope (TEM), Raman spectroscopy and FT-IR. The results showed that the functionalization and chemical compatibility of APTES-treated MWCNTs with epoxy composition provides their best dispersion in the epoxy composition, had important influence on curing behavior, structure and physicochemical properties of the epoxy composites plasticized with trichloroethyl phosphate. The results showed that the functionalization and chemical compatibility of APTES-treated MWCNTs with epoxy composition provides increased of physicomechanical properties of epoxy composites: bending stress increases by 194% and bending modulus increases by 137%, the tensile strength increases by 108% and the tensile elastic modulus increases by 52%, impact strength increases by 300%, in comparison with plasticized epoxy composite that does not contain MWCNTs.