Zinc phthalocyanine tetrasulfonate-loaded polyelectrolytic PLGA nanoparticles for photodynamic therapy applications
Maria Cristina Modesto Clementino de Toledo1, Alexandro da Silva Abreu2, Janicy Arantes Carvalho2
1Organic Synthesis Laboratory, Research and Development Institute - IPD, Vale do Paraíba University, Av. Shishima Hifumi 2911, CEP 12244-000, São José dos Campos, Brazil.
Background:
Photodynamic Therapy (PDT) is a modality for the treatment of neoplastic tissues, which is based on the administration of a phototherapeutic agent and light irradiation at an appropriate wavelength, aiming to locate and destroy the target cell with the formation of reactive oxygen species. Nanoencapsulation technology presents itself as a tool for incorporation of bioactive substances aiming to improve their solubility in physiological environment, obtain a longer circulation time in the organism, administration of lower dosages and the minimization of side effects. The present work aimed at the development of poly (lactic acid-glycolic acid) (PLGA) nanoparticles coated with polyelectrolyte film layers for encapsulating zinc phthalocyanine tetrasulfonated (ZnPcSO4) as a bioactive substance model.
Methods:
PLGA nanoparticles were produced by the double emulsion/solvent evaporation technique and polyelectrolytic coating was performed using polyalkylamine hydrochloride (PAH) as a weak polycation and poly (4-styrene sulfonate) (PSS) as a strong polyanion by layer-by-layer self-assembly technique (known as layer-by-layer-LbL). The nanoparticulate system was studied by scanning electron microscopy, steady-state, and their biological activity was evaluated using in vitro cancer cell lines by classical MTT assay.
Results:
The polyelectrolytic PLGA nanoparticles had an average diameter of 384.7 ± 138.6 nm, restricted distribution size with a polydispersity index. The obvious change in zeta potential indicates successful alternation in polycation (PAH) and polyanion (PSS) deposition directly in PLGA nanoparticles. Scanning electron microscopy (SEM) analysis showed that the formed system had morphology spherical, typical of these release systems. The loading efficiency was 82.1 % ± 1.2 %. The polyelectrolytic nanoparticles loaded with phthalocyanine maintained their photophysical behavior after encapsulation. Cell viability was determined, obtaining 90 % cell death.
Conclusions:
Therefore, the presented work depicts ZnPcSO4-loaded polyelectrolytic PLGA nanoparticles as a promise drug delivery system for phototherapeutic agent, which are thus expected to have superior therapeutic efficiency than free drug.