Holographic Photopolymer Material with High Dynamic Range (Δn) via Thiol-Ene Click Chemistry

A high-performance holographic recording medium was developed based on a unique combination of photoinitiated thiol-ene click chemistry and functional, linear polymers used as binders. Allyl reactive sites were incorporated along the backbone of the linear polymer binder to enable facile film casting and to facilitate cross-linking by photopolymerization of the thiol-ene monomers that also serve as the writing monomers in this distinctive approach to holographic materials. The allyl content and the ratio of the linear polymer to the writing monomers were varied to maximize and control the refractive index contrast. A blade-coating-based film preparation method was developed to form films from the mixture of linear polymer and the thiol-ene monomers. This approach results in a holographic material with a peak to mean index contrast (Δn) that reaches 0.04. The refractive index contrast was stable for at least two weeks. Haze in holograms with a high writing monomer loading was significantly reduced when a higher allyl content was incorporated into the binder, resulting in the lowest haze around 0.2%. Finally, the media exhibit high resolution as demonstrated by the ability to record reflection holograms with 140 nm pitch and diffraction efficiency in excess of 90%.