Nitrogen-doped carbon quantum dots conjugated isoreticular metal-organic framework-3 particles based luminescent...

Amine group-containing isoreticular metal-organic framework (IRMOF-3) particles are utilized for the first time as a trinitrotoluene (TNT) sensing material. IRMOF-3 particles are synthesized using zinc nitrate as a metal precursor and 2-amino-1,4-benzenedicarboxylic acid as a linker. The nitrogen-doped carbon quantum dots (NCQDs) are synthesized from citric acid and ethylenediamine as carbon and nitrogen precursor, respectively. The NCQDs are conjugated with IRMOF-3 particles as IRMOF-3/NCQDs. The TEM micrograph revealed the average size of IRMOF-3 particles to be 363.66 nm. The photoluminescence emission intensity of IRMOF-3 particles at λ_em 430 nm is highly increased in the presence of NCQDs (λ_ex 330 nm). Both the as-synthesized IRMOF-3 and IRMOF-3/NCQD particles are explored for TNT detection to compare the effect of NCQDs on the IRMOF-3 particle surface. Lower limit of detection (7.5 × 10^-8 M) and higher Stern-Volmer constant (4.46 × 10⁶ M^-1) are achieved by IRMOF-3/NCQD particles. The association constant also increased from 5.3 × 10⁴ to 2.78 × 10⁶ M^-1 after the conjugation of IRMOF-3 particles with NCQDs. Moreover, enhanced selectivity for TNT over trinitrophenol is achieved using the IRMOF-3/NCQD particles. Graphical Abstract.