Bioresorbable magnesium-reinforced PLA membrane for guided bone/tissue regeneration

Considering the inferior mechanical properties of the current bioresorbable polymers, a novel bioresorbable magnesium-reinforced polylactide (PLA) membrane was designed for the application in critical defect sites in guided bone/tissue regeneration. The PLA-FAZ91 membrane was fabricated by combining two PLA membranes with a fluoride-coated AZ91 (9 wt% Al, 1 wt% Zn) (FAZ91) magnesium alloy core by hot pressing. A combined double-layered PLA membrane was used as the control group. A three-point bending test was performed to compare their maximum load and stiffness. Samples were immersed in the HBSS for 20 weeks, and their weight loss percentages were recorded, and a three-point bending test was performed after immersion. An ion release test was performed by immersing samples in the HBSS for 4 weeks and determining the pH and ion concentrations of the HBSS. Cell viability was tested by culturing pre-osteoblast cells with sample extracts in the culture medium obtained from degraded samples. As a result, PLA-FAZ91 showed a significantly higher maximum load and stiffness than those of the non-reinforced PLA membrane. The weight loss of PLA-FAZ91 was much faster, as FAZ91 showed major degradation and was completely degraded after 16-20 weeks of immersion. The degradation of the PLA wrap was accelerated by FAZ91. The mechanical superiority of PLA-FAZ91 over PLA endured for at least 3 weeks during immersion. The pH, magnesium- and fluoride-ion concentration in the PLA-FAZ91 group increased at an appropriate rate. The cell viability was not adversely affected by the addition of FAZ91 to PLA. Therefore, the bioresorbable magnesium-reinforced PLA membrane has the potential to be used as a good alternative to pure PLA membrane in guided bone/tissue regeneration.