Comparative Analysis of Biofilm Formation on Materials Used for the Fabrication of Implant-Supported Prostheses

The purpose of this study was to compare biofilm formation on materials used for the fabrication of implant-supported dental prostheses. Twenty discs (D=15 mm, H=3 mm) were fabricated from one of the following restorative materials: yttria tetragonal zirconia polycrystal (Y-TZP); commercially pure titanium (CP-Ti); or heat-cured polymethyl methacrylate (PMMA). Specimens were polished following standard protocols. A non-contact profilometer (NPFLEX, Bruker, UK) was used to assess the surface roughness of each disk; results were reported as Ra (µm). Five strains of Gram-negative bacteria frequently associated with peri-implantitis, Aggregatibacter actinomycetemcomitans, Candida. albicans, Porphyromonas gingivalis, Prevotella intermedia, and Tannerella forsythia, were cultured on hand-polished discs fabricated from heat-cured PMMA, Y-TZP, or CP-Ti to compare biofilm formation on each type of material. The results were reported as colony-forming units per milliliter (CFU/mL). One-way ANOVA and post hoc tests were used to compare surface roughness and bacterial colonization on the respective materials. Statistical significance was set at a = 0.05. Discs fabricated from Y-TZP had a significantly higher Ra value (350 ± 30 µm) than either PMMA, or CP-Ti discs. Discs fabricated from either Y-TZP and CP-Ti may exhibit less colonization by bacteria associated with peri-mucositis and peri-implantitis. Y-TZP and CP-Ti are suggested materials for fabrication of implant-supported prostheses, considering biofilm formation.