Failure Analysis of the Tree Column Structures Type AlSi10Mg Alloy Branches Manufactured by Selective Laser Melting

Peikang Bai1, Pengcheng Huo1, Taotao Kang2

  • 1School of Materials Science and Engineering, North University of China, Taiyuan 030051, China.

Materials (Basel, Switzerland)
|September 11, 2020
PubMed

Keywords:
AlSi10Mg alloy branchesSi content distributiondimplesfractureselective laser melting (SLM)stress

More Related Videos

Indirect Fabrication of Lattice Metals with Thin Sections Using Centrifugal Casting08:32

Indirect Fabrication of Lattice Metals with Thin Sections Using Centrifugal Casting

Published on: May 14, 2016

12.8K
Experimental Procedure for Warm Spinning of Cast Aluminum Components07:36

Experimental Procedure for Warm Spinning of Cast Aluminum Components

Published on: February 1, 2017

9.8K

Related Concept Videos

Design of Columns under a Centric Load01:17

Design of Columns under a Centric Load

The design of columns under centric load is a fundamental aspect of structural engineering and is critical for ensuring the stability and integrity of structures. Euler's and Secant's formulas are central to understanding and calculating the critical load and deformation behaviors of columns, providing a basis for safe and effective structural design.
Euler's formula is applicable under the assumption that the column is a perfect, straight, homogenous prism, and it is operating...
415
Prismatic Beams: Problem Solving01:15

Prismatic Beams: Problem Solving

In the design of a supported timber beam subjected to a distributed load, both the beam's physical dimensions and the timber's characteristics, such as its grade and species, are critical. These factors determine the allowable stress values, which are crucial for calculating the necessary beam depth to ensure structural integrity and safety.
The design begins with analyzing the beam as a free body to identify moments and force balances, thereby determining support reactions. Next, the...
359
Design of Columns under an Eccentric Load01:21

Design of Columns under an Eccentric Load

Designing columns to withstand eccentric loads is a critical aspect of structural engineering, ensuring structures can support off-center loads without failure. This design process must account for the additional normal stresses introduced by eccentric loading, which can significantly influence a column's stress distribution and overall stability. An eccentric load applied to a column induces normal stresses that can be conceptualized as a combination of stresses due to an equivalent...
997
Lumber Defects01:23

Lumber Defects

Lumber defects, which can affect both the appearance and structural integrity of wood, include a variety of growth and manufacturing flaws. Growth defects such as knots and knotholes occur where branches were once attached to the tree trunk, with knotholes forming when these knots fall out. Other natural defects include decay and insect damage, which compromise the wood's strength and durability.
Shakes are minor fractures that run along or across the wood's annual rings, while wane is...
387
Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
1.7K
Unsymmetric Loading of Thin-Walled Members01:23

Unsymmetric Loading of Thin-Walled Members

Thin-walled members with non-symmetrical cross-sections are vital to engineering structures, offering material efficiency and structural integrity. However, unsymmetrical loading on these members leads to complex stress distributions, resulting in simultaneous bending and twisting can cause deformation or structural failure. The interaction between bending and twisting requires detailed analysis to ensure structural resilience.
The concept of the shear center is crucial in countering the...
309